Steel And Metal Putty

Product Details:

Zorrik 301 Rapid Steel Putty is a room temperature cure steel reinforced two-part epoxy repair putty cures rapidly, facscilitating to emergency repairs to various metals. 
Features:
Cures rapidly in 5 minutes at room temperature- Saves downtime
Non Sag, No Shrink
Cures to metal luster finish
Excellent adhesion to metals like steel, cast iron, stainless steel, concrete, copper, aluminium, and bonze.
Application:
Emergency leakages repair of BF water cooling jacket and water pipes.
Oil leakages in Transformers, Pipe line, elbows and gear box flanges
Leakage arresting of coal mill gear box flanges
Filling of pitting holes & stripped threads.
Other Details:
Fast coating epoxy resin part-A
Fast curing epoxy hardner Part-B

Product Details:

Two component room temperature cure, easy-to-use epoxy putty in the form of a co-extruded cocentric stick.M-SEAL STEEL PUTTY is useful to seal, grip, join and insulate a variety of surfaces like ferrous and non-ferrous metals, etc. On curing, exhibits tough and long lasting bond. Cured product is resistant to moisture, heat, mild acids and alkalis.
Features:
Cures in 10 to 20 minutes at room temperature
Co-centric stick – Convenient to use, cut required quantity and use
Best for salty and humid environments, heat resistant up to 120C
Cured product can be drilled, filed, tapped, machined, cut and then painted.
Application:
Sealing of leakage/cracks in metal fabrications, industrial vessels, boilers, hulls of ships, boats and trawlers.
Sealing water supply mains, storage tanks, concrete sewer pipes, heat exchanger coils, etc.
Sealing blowholes, cracks, and leakage in ferrous and non-ferrous casting, pumps and mould boxes etc.
Sealing holes/cracks in wooden and metal patterns.
Repairing of damaged internal threads of various types of machine pumps.
Sealing cracks in casings of meters/gear-box etc.
Repairing heat exchangers and condensers
Tank linings and chutes, Agitator Shafts,Slurry Lines,Spiral Classifiers
Resurfacing and repairing rudders and pintel housings
Repairing of cooling pump impellers & Butterfly valves
Other Details:
Seals joins fixes builds
Hand moldable epoxy putty

Product Details:

Zorrik 311 Premium Metal Putty is a two-part Ferro-silicon filled epoxy resin system, engineered to highly machinable and good corrosion resistance to mild chemical attack.
Features:
Contains no iron or steel fillers.
Corrosion is eliminated due to high Ferro-silicon content during service time.
Epoxy resin base – Excellent adhesion to steel, and cast iron.
Superior machining finished surface
Tolerance- Facilitates fine tolerance limits.
Excellent resistance to a variety of chemicals.
Corrosion resistant
High strength epoxy hardner 
Application:
Shaft: Restoring tolerance to worn shafts.
Bearing seats and housings.
Motor end covers
Key ways
Thinned pipes, tubes sections.
Engine blocks
Pump casings and impeller.
Rebuilding of water, coal slurry pump casings,

Product Details:

DESCRIPTION:

ZORRIK 421 is a trowelable, high-performance solvent free 2K polymer composite containing graded sintered ceramic particles in an epoxy resin, and has highest standards of elevated temperature service, chemical resistance, abrasion resistance, and corrosion protection for steel surface.

The polymer composite comprises sintered ceramic of extreme hardness and resistance to abrasion for the treatment of steel applications where temperatures go up to 300° Celsius or the substrate requires protection from high abrasion. The surface finish may be applied as a thin film with 5mm recommended to be the minimum. It is acceptable to apply high builds in most situations to maximize life.

PRODUCT FEATURES:

✓ Highly corrosion resistant polymer system
✓ Free of all solvents - zero VOC
✓ Engineered for high mechanical strength.
✓ Resistant to organic solvents
✓ Temperature resistance up to 300°C.
✓ Outstanding resistance to chemicals & acids
✓ Excellent resistance to sliding abrasion.
✓ Suitable as an adhesive for Ceramic Tiles
✓ Tough polymer with high adhesive strength
✓ Engineered for high mechanical strength. 

APPLICATION AREAS:

• Exhaust Stacks
• Tanks & Vessels
• Flanges
• Bearing Faces
• Pumps & Impellors
• Ducting Systems
• Rail Cars
• Scrubbers
• Laundries
• Steelwork Coating
• Pipelines & Valves
• Solvent Extraction 

ENVIRONMENTAL CONDITIONS:
• Substrate temperature should be at least 3°C above dew point but not above 50°C
• Relative humidity should be below 85%

APPLICATION METHOD:

Mixing of product should be carried out using slow speed mixers or spatulas and completed by adding to the Part “A”, the Part “B”. Ensure the mix is homogenous and free from lumps. Application can be carried out by applying mixed compound directly to the desired area or component with gloved hands or by tools such as paint scrapers, putty knives or flat steel trowels, the latter mainly for large horizontal areas. Application can be carried out with relative ease on vertical or horizontal surfaces. Initially apply the scratch coat i.e. a very thin layer to wet the entire surface and avoid air entrapment. The pot life and cure time depends on temperature and mass of the mix; the higher the temperature and larger the mass, faster is the cure and shorter the pot life.

SHELF LIEF:

2 Years from the date of manufacture.